Introduction

   Wood in building applications is gaining importance. Consumers are choosing wood predominantly due to environmental awareness and positive health impacts. In order to use wood in moist and outdoor applications, the durability characteristic must meet the specified criteria. Restrictions on many classic biocides due to environmental and health concerns, and negative public opinion on the existing biocides and the use of tropical timber, have altered research philosophies to improve the durability and service life of wood. Unfortunately, the majority of wood species in Europe are not durable; therefore, we need to understand the performance of wood better or develop alternative treatments to improve relevant properties of wood through processes such as wood modification.

   The objective of study was to elucidate the influence of natural and artificial weathering on durability classification according to EN 350 as well as on the material resistance and wetting ability. These two parameters were used to calculate the durability of wood according to the Meyer-Veltrup model. This model has already been successfully applied and validated on naturally durable wood species and modified wood.

Material and methods

   The wood species chosen for this research are important in Europe: sweet chestnut heartwood (Castanea sativa), oak heartwood (Quercus sp.), European beech wood (Fagus sylvatica), Scots pine heartwood and sapwood (Pinus sylvestris), European larch heartwood (Larix decidua) and, Norway spruce (Picea abies). Norway spruce served as the reference in some novel service life prediction models . Defect-free cube blocks (1.5 cm × 2.5 cm × 5.0 cm) were cut as prescribed in European standard EN 113. Some of the materials were treated with a copper-based wood preservative or thermally modified. The experiment was performed on five replicates per treatment. There were 275 samples prepared for this analysis.

Treatment of specimens

   Eleven different materials were prepared for this experiment. The thermal modification was performed for three hours at 230°C on Norway spruce and 215°C on beech wood according to the commercial Silvapro® process for each species.

Ageing procedures

   Artificial accelerated weathering (AAW) and outdoor ageing, with three different exposure times, were applied. AAW was carried out in a chamber (ATLAS UP, Suntest XXL+, Linsengericht, Germany). The specimens were exposed to alternating cycles of elevated temperature (38°C) and relative humidity (68%) with UV radiation (0.35 W/m2) and artificial rain for 1000 h.

Results and discussion

   Mass changes are the most basic indicators of changes in wood specimens during artificial or natural weathering. Artificial weathering resulted in mass losses comparable to 9–18 months of natural weathering.

Conclusions

   Artificial and natural weathering resulted in the leaching of extractives from wood, which negatively influenced inherent durability, as evident from the mass losses caused by G. trabeum. Weathering negatively influenced moisture resistance. This phenomenon was evident for non-treated, copper impregnated and modified wood species. This was reflected in the decreased relative resistance dose and was evident for all tested materials. The most notable decreases were noted for thermally modified wood, Scots pine heartwood, larch and sweet chestnut heartwood.

                                          Завдання №3

Вступ

   Дерево в будівництві набуває все більшого значення. Споживачі вибирають деревину переважно через екологічну обізнаність та позитивний вплив на здоров’я. Щоб використовувати деревину у вологих і зовнішніх приміщеннях, характеристика довговічності повинна відповідати зазначеним критеріям. Обмеження щодо багатьох класичних біоцидів через проблеми з навколишнім середовищем та здоров’ям, а також негативна громадська думка щодо існуючих біоцидів та використання тропічної деревини змінили філософію досліджень, щоб покращити довговічність та термін служби деревини. На жаль, більшість порід деревини в Європі не довговічні; тому ми повинні краще розуміти характеристики деревини або розробити альтернативні способи обробки для покращення відповідних властивостей деревини за допомогою таких процесів, як модифікація деревини.

   Метою дослідження було з'ясувати вплив природного та штучного вивітрювання на класифікацію довговічності згідно з EN 350, а також на стійкість матеріалу та змочувальну здатність. Ці два параметри були використані для розрахунку довговічності деревини за моделлю Мейєра-Велтрупа. Ця модель вже була успішно застосована та перевірена на натуральних породах деревини та модифікованої деревині.

Матеріал і методи

   Вибрані для цього дослідження породи є важливими для Європи: серцевина каштана (Castanea sativa), серцевина дуба (Quercus sp.), деревина бука європейського (Fagus sylvatica), ядро ​​сосни звичайної та заболонь (Pinus sylvestris), ядро ​​​​європейської модрини ( Larix decidua) і ялина звичайна (Picea abies). Норвезька ялина служила еталоном у деяких нових моделях прогнозування терміну служби. Бездефектні кубічні блоки (1,5 см × 2,5 см × 5,0 см) були вирізані, як передбачено європейським стандартом EN 113. Деякі матеріали були оброблені консервантом для деревини на основі міді або термічно модифікованими. Експеримент проводили у п’яти повторах за одну обробку. Для цього аналізу було підготовлено 275 зразків.